Technical Data
产品说明
ASTALAC™ ABS DMT is a high melt flow impact toughened ABS injection moulding grade designed for use in thin wall applications. ASTALAC™ DMT offers an optimum balance of impact toughness, rigidity, heat resistance and mouldability. Typical applications include telecommunications equipment such as telephones casings, telephone handsets as well as telephone cable clips and fittings.
Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ DMTUV ].
总体
材料状态 • 已商用:当前有效
资料 1 • Technical Datasheet (English)
UL 黄卡 2 • E183535-226902
搜索 UL 黄卡 • Marplex Australia Pty. Ltd.
• ASTALAC™
供货地区 • 北美洲 • 南美洲 • 亚太地区
添加剂 • 冲击调节器
性能特点 • 改良抗撞击性 • 良好的成型性能 • 耐热性,中等
• 抗撞击性,良好 • 流动性高 • 中等硬度
用途 • 薄壁部件 • 通讯器材
加工方法 • 注射成型
物理性能 额定值单位制 测试方法
比重 1.03g/cm³ ASTM D792
熔流率 (230°C/3.8 kg) 8.0g/10 min ASTM D1238
收缩率 - 流动 (3.00 mm) 0.40 到 0.80% ASTM D955
吸水率 (24 hr) 0.25% ASTM D570
机械性能 额定值单位制 测试方法
抗张强度 4 (3.20 mm) 42.0MPa ASTM D638
伸长率 4 (断裂, 3.20 mm) 30% ASTM D638
弯曲模量 5 (3.20 mm) 2350MPa ASTM D790
弯曲强度 5 (3.20 mm) 70.0MPa ASTM D790
冲击性能 额定值单位制 测试方法
悬壁梁缺口冲击强度 (3.20 mm) 250J/m ASTM D256
硬度 额定值单位制 测试方法
洛氏硬度 (R 计秤) 100 ASTM D785
热性能 额定值单位制 测试方法
热变形温度 ASTM D648
1.8 MPa, 未退火, 3.20 mm 76.0°C
1.8 MPa, 未退火, 12.7 mm 86.0°C
维卡软化温度 103°C ASTM D1525 6
线形膨胀系数 - 流动 0.000088cm/cm/°C ASTM D696
可燃性 额定值单位制 测试方法
UL 阻燃等级 (1.60 mm) HB UL 94
热灯丝点火温度 (1.60 mm) 550°C AS/NZS 60695
注射 额定值单位制
干燥温度 85.0 到 90.0°C
干燥时间 3.0 到 6.0hr
螺筒后部温度 200 到 220°C
螺筒中部温度 210 到 230°C
螺筒前部温度 220 到 240°C
加工(熔体)温度 215 到 245°C
ASTALAC™ ABS DMT
丙烯腈丁二烯苯乙烯
Marplex Australia Pty. Ltd.
注射 额定值单位制
模具温度 40.0 到 70.0°C
注塑温度 60.0 到 140MPa
注射速度 中等
背压 0.100 到 0.500MPa
螺杆转速 40 到 60rpm
合模力 3.0 到 6.0kN/cm²
|