ASTALAC™ ABS KMS
丙烯腈丁二烯苯乙烯
Marplex Australia Pty. Ltd.
Technical Data
产品说明
ASTALAC™ ABS KMS was upgraded in November 2007 to comply with RoHS and is a high impact strength flame retardant grade of ABS designed for sheet extrusion applications requiring flame retardancy, superior toughness and abuse resistance whilst maintaining a balance of high gloss, easy formability and product rigidity. Typical thermoformed applications include large air conditioner/heater unit casings and advertising signage blanks.
Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ ABS KMSUV ].
总体
材料状态 • 已商用:当前有效
资料 1 • Technical Datasheet (English)
搜索 UL 黄卡 • Marplex Australia Pty. Ltd.
• ASTALAC™
供货地区 • 北美洲 • 南美洲 • 亚太地区
添加剂 • 阻燃
性能特点 • 光泽,高 • 韧性良好 • 阻燃性能
• 抗撞击性,高 • 中等硬度
用途 • 片材
RoHS 合规性 • RoHS 合规
加工方法 • 片材挤出成型 • 热成型
物理性能 额定值单位制 测试方法
比重 1.15g/cm³ ASTM D792
熔流率 (230°C/3.8 kg) 1.5g/10 min ASTM D1238
收缩率 - 流动 (3.00 mm) 0.40 到 0.80% ASTM D955
吸水率 (24 hr) 0.25% ASTM D570
机械性能 额定值单位制 测试方法
抗张强度 3 (3.20 mm) 36.0MPa ASTM D638
伸长率 3 (断裂, 3.20 mm) 50% ASTM D638
弯曲模量 4 (3.20 mm) 2050MPa ASTM D790
弯曲强度 4 (3.20 mm) 62.0MPa ASTM D790
冲击性能 额定值单位制 测试方法
悬壁梁缺口冲击强度 (3.20 mm) 400J/m ASTM D256
落锤冲击 (3.20 mm) 40.0J ASTM D3029
硬度 额定值单位制 测试方法
洛氏硬度 (R 计秤) 86 ASTM D785
热性能 额定值单位制 测试方法
热变形温度 ASTM D648
1.8 MPa, 未退火, 3.20 mm 72.0°C
1.8 MPa, 未退火, 12.7 mm 84.0°C
维卡软化温度 98.0°C ASTM D1525 5
线形膨胀系数 - 流动 0.000090cm/cm/°C ASTM D696
可燃性 额定值单位制 测试方法
热灯丝点火温度 (1.60 mm) 960°C AS/NZS 60695
挤出 额定值单位制
干燥温度 85.0 到 90.0°C
干燥时间 3.0 到 5.0hr
第1气缸区温度 170 到 190°C
第2气缸区温度 175 到 200°C
第3气缸区温度 180 到 205°C
第4气缸区温度 185 到 210°C
ASTALAC™ ABS KMS
丙烯腈丁二烯苯乙烯
Marplex Australia Pty. Ltd.
挤出 额定值单位制
第5气缸区温度 190 到 220°C
熔体温度 190 到 230°C
模具温度 180 到 220°C
牵引辊 75.0 到 105°C
背压 10.0 到 25.0MPa
|