ASTALAC™ ABS M112LG is an ultra high heat resistance low gloss grade of ABS and is designed for injection moulding applications requiring a balance of reduced gloss, high heat resistance, impact toughness, product rigidity and mouldability. Typical applications in the automotive area include interior heater air vents and barrels, rear seat upper mouldings and T-Bar surround assemblies.
Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ ABS M112LGW ].
总体
材料状态 • 已商用:当前有效
资料 1 • Technical Datasheet (English)
搜索 UL 黄卡 • Marplex Australia Pty. Ltd.
• ASTALAC™
供货地区 • 北美洲 • 南美洲 • 亚太地区
性能特点 • 光泽,低 • 良好的成型性能 • 中等硬度
• 抗撞击性,良好 • 耐热性,高
用途 • 汽车领域的应用: • 汽车内部零件
加工方法 • 注射成型
物理性能 额定值单位制 测试方法
比重 1.05g/cm³ ASTM D792
熔流率 (220°C/10.0 kg) 2.0g/10 min ASTM D1238
收缩率 - 流动 (3.00 mm) 0.40 到 0.80% ASTM D955
吸水率 (24 hr) 0.25% ASTM D570
机械性能 额定值单位制 测试方法
抗张强度 3 (3.20 mm) 46.0MPa ASTM D638
伸长率 3 (断裂, 3.20 mm) 50% ASTM D638
弯曲模量 4 (3.20 mm) 2550MPa ASTM D790
弯曲强度 4 (3.20 mm) 78.0MPa ASTM D790
冲击性能 额定值单位制 测试方法
悬壁梁缺口冲击强度 (3.20 mm) 150J/m ASTM D256
硬度 额定值单位制 测试方法
洛氏硬度 (R 计秤) 104 ASTM D785
热性能 额定值单位制 测试方法
热变形温度 ASTM D648
1.8 MPa, 未退火, 3.20 mm 91.0°C
1.8 MPa, 未退火, 6.40 mm 98.0°C
1.8 MPa, 未退火, 12.7 mm 105°C
维卡软化温度 119°C ASTM D1525 5
线形膨胀系数 - 流动 0.000085cm/cm/°C ASTM D696
可燃性 额定值单位制 测试方法
UL 阻燃等级 (1.60 mm) HB UL 94
热灯丝点火温度 (1.60 mm) 550°C AS/NZS 60695.2.12
注射 额定值单位制
干燥温度 90.0 到 95.0°C
干燥时间 3.0 到 6.0hr
螺筒后部温度 215 到 235°C
螺筒中部温度 225 到 245°C
螺筒前部温度 235 到 255°C
加工(熔体)温度 230 到 260°C
模具温度 30.0 到 60.0°C
注塑温度 60.0 到 140MPa
ASTALAC™ ABS M112LG
丙烯腈丁二烯苯乙烯
Marplex Australia Pty. Ltd.
注射 额定值单位制
注射速度 中等
背压 0.100 到 0.500MPa
螺杆转速 40 到 60rpm
合模力 3.0 到 6.0kN/cm²
|