Technical Data
产品说明
ASTALAC™ ABS MGF10E is a 10% short fibre length glass filled ABS grade designed for extrusion or moulding into thick sections. This grade features improved rigidity & tensile strength compared to standard ABS extrusion grades, together with a reduced thermal expansion coefficient. These properties are preliminary only, pending full manufacturing runs.
Note: The letters "UV" indicate additional UV stabilisation has been added [ ie: ASTALAC™ ABS MGF10EUV ].
总体
材料状态 • 已商用:当前有效
资料 1 • Technical Datasheet (English)
搜索 UL 黄卡 • Marplex Australia Pty. Ltd.
• ASTALAC™
供货地区 • 北美洲 • 南美洲 • 亚太地区
填料/增强材料 • 玻璃纤维增强材料, 10% 填料按重量
用途 • 厚壁配件
加工方法 • 挤出
物理性能 额定值单位制 测试方法
比重 1.11g/cm³ ASTM D792
熔流率 (220°C/10.0 kg) 6.0g/10 min ASTM D1238
收缩率 - 流动 (3.00 mm) 0.20 到 0.40% ASTM D955
吸水率 (24 hr) 0.10% ASTM D570
机械性能 额定值单位制 测试方法
抗张强度 3 (3.20 mm) 61.0MPa ASTM D638
伸长率 3 (断裂, 3.20 mm) 5.0% ASTM D638
弯曲模量 4 (3.20 mm) 3250MPa ASTM D790
弯曲强度 4 (3.20 mm) 88.0MPa ASTM D790
冲击性能 额定值单位制 测试方法
悬壁梁缺口冲击强度 (3.20 mm) 120J/m ASTM D256
硬度 额定值单位制 测试方法
洛氏硬度 (R 计秤) 104 ASTM D785
热性能 额定值单位制 测试方法
热变形温度 ASTM D648
1.8 MPa, 未退火, 3.20 mm 92.0°C
1.8 MPa, 未退火, 6.40 mm 97.0°C
1.8 MPa, 未退火, 12.7 mm 102°C
维卡软化温度 106°C ASTM D1525 5
线形膨胀系数 - 流动 0.000040 到 0.000070cm/cm/°C ASTM D696
可燃性 额定值单位制 测试方法
UL 阻燃等级 (1.60 mm) HB UL 94
热灯丝点火温度 (1.60 mm) 550°C AS/NZS 60695
挤出 额定值单位制
干燥温度 85.0 到 90.0°C
干燥时间 3.0 到 6.0hr
第1气缸区温度 170 到 190°C
第2气缸区温度 175 到 200°C
第3气缸区温度 180 到 205°C
第4气缸区温度 185 到 210°C
第5气缸区温度 190 到 220°C
熔体温度 190 到 230°C
ASTALAC™ ABS MGF10E
丙烯腈丁二烯苯乙烯
Marplex Australia Pty. Ltd.
挤出 额定值单位制
模具温度 180 到 220°C
牵引辊 75.0 到 105°C
背压 10.0 到 25.0MPa
备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料;不过您可以从供应商处了解最新资料。
2 一般属性:这些不能被视为规格。
3 5.0 mm/min
4 1.3 mm/min
5 压 力1 (10N)
|