ASTALAC™ ABS X15
丙烯腈丁二烯苯乙烯
Marplex Australia Pty. Ltd.
Technical Data
产品说明
ASTALAC™ ABS X15 is a high heat resistance grade of ABS and is designed for injection moulding applications requiring a balance of heat resistance, impact toughness, product rigidity and mouldability. Typical automotive applications include interior console assemblies, glove-box lids, door-liner armrest substrate mouldings, wiper blade refill strips and whitegoods fascia panels.
Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ ABS X15UV ].
总体
材料状态 • 已商用:当前有效
资料 1 • Technical Datasheet (English)
搜索 UL 黄卡 • Marplex Australia Pty. Ltd.
• ASTALAC™
供货地区 • 北美洲 • 南美洲 • 亚太地区
性能特点 • 抗撞击性,良好 • 耐热性,高
• 良好的成型性能 • 中等硬度
用途 • 大型家用电器和小型家用电器 • 汽车领域的应用:
加工方法 • 注射成型
物理性能 额定值单位制 测试方法
比重 1.05g/cm³ ASTM D792
熔流率 ASTM D1238
220°C/10.0 kg 7.0g/10 min
230°C/3.8 kg 2.0g/10 min
收缩率 - 流动 (3.00 mm) 0.40 到 0.80% ASTM D955
吸水率 (24 hr) 0.25% ASTM D570
机械性能 额定值单位制 测试方法
抗张强度 3 (3.20 mm) 44.0MPa ASTM D638
伸长率 3 (断裂, 3.20 mm) 35% ASTM D638
弯曲模量 4 (3.20 mm) 2400MPa ASTM D790
弯曲强度 4 (3.20 mm) 72.0MPa ASTM D790
冲击性能 额定值单位制 测试方法
悬壁梁缺口冲击强度 (3.20 mm) 200J/m ASTM D256
硬度 额定值单位制 测试方法
洛氏硬度 (R 计秤) 106 ASTM D785
热性能 额定值单位制 测试方法
热变形温度 ASTM D648
1.8 MPa, 未退火, 3.20 mm 85.0°C
1.8 MPa, 未退火, 6.40 mm 93.0°C
1.8 MPa, 未退火, 12.7 mm 100°C
维卡软化温度 115°C ASTM D1525 5
线形膨胀系数 - 流动 0.000080cm/cm/°C ASTM D696
可燃性 额定值单位制 测试方法
UL 阻燃等级 (1.60 mm) HB UL 94
热灯丝点火温度 (1.60 mm) 550°C AS/NZS 60695
注射 额定值单位制
干燥温度 90.0 到 95.0°C
干燥时间 3.0 到 6.0hr
螺筒后部温度 215 到 235°C
螺筒中部温度 225 到 245°C
螺筒前部温度 235 到 255°C
加工(熔体)温度 230 到 260°C
ASTALAC™ ABS X15
丙烯腈丁二烯苯乙烯
Marplex Australia Pty. Ltd.
注射 额定值单位制
模具温度 40.0 到 80.0°C
注塑温度 60.0 到 140MPa
注射速度 中等
背压 0.100 到 0.500MPa
螺杆转速 40 到 60rpm
合模力 3.0 到 6.0kN/cm²
|