丙烯腈丁二烯苯乙烯

 

INEOS ABS (USA)

 

产品说明

 

Lustran ABS LGA resin is a low-gloss grade of ABS (acrylonitrile butadiene styrene). This automotive injection molding grade offers an excellent balance of rigidity, impact strength, and abuse resistance. The resin is available in natural and black colors only. The consistent, clean, natural color of LGA makes it ideally suitable for use with color concentrates.

 

Lustran ABS LGA resin is designed to meet stringent physical property and appearance requirements for low-loss automotive interior trim applications. Typical uses are pillar posts, consoles, scuff plates, map pockets, and interior quarter trim panels. As with any product, use of Lustran ABS LGA resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet (English)

 

UL 黄卡 2 •  E44741-235659

 

搜索 UL 黄卡 •  INEOS ABS (USA)

 

•  Lustran® ABS

 

 

 

供货地区

 

特性

 

用途

 

机构评级

 

外观

 

形式

 

加工方法

 

多点数据

 

 

 

• 北美洲

• 刚性，高 • 光泽，低 • 抗撞击性，良好

• 汽车领域的应用 • 汽车内部零件

• EC 1907/2006 (REACH)

• 黑色 • 自然色

• 粒子

• 注射成型

• Isochronous Stress vs. Strain • Isothermal Stress vs. Strain • Secant Modulus vs. Strain (ISO

(ISO 11403-1) (ISO 11403-1) 11403-1)

 

 

物理性能 额定值单位制 测试方法

比重 1.05g/cm³ ASTM D792

特定体积 0.950cm³/g ASTM D792

熔流率（熔体流动速率） ASTM D1238

220°C/10.0 kg 21g/10 min

230°C/3.8 kg 7.0g/10 min

收缩率 - 流动 0.40 到 0.70% ASTM D955

机械性能 额定值单位制 测试方法

拉伸模量 2210MPa ASTM D638

抗张强度

屈服 36.5MPa ASTM D638

屈服 39.0MPa ISO 527-2

弯曲模量

-- 2410MPa ASTM D790

-- 2430MPa ISO 178

弯曲强度 (屈服) 72.4MPa ASTM D790

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度

23°C, 3.18 mm 170J/m ASTM D256

-40°C 4 7.7kJ/m² ISO 180/1A

23°C 4 16kJ/m² ISO 180/1A

硬度 额定值单位制 测试方法

洛氏硬度 (R 级) 105 ASTM D785

 

 

 

 

 

 

Lustran® ABS LGA

丙烯腈丁二烯苯乙烯

INEOS ABS (USA)

热性能 额定值单位制 测试方法

载荷下热变形温度 ASTM D648

0.45 MPa, 未退火, 3.18 mm 90.0°C

0.45 MPa, 未退火, 12.7 mm 92.2°C

0.45 MPa, 退火, 3.18 mm 100°C

0.45 MPa, 退火, 12.7 mm 102°C

1.8 MPa, 未退火, 3.18 mm 76.1°C

1.8 MPa, 未退火, 12.7 mm 87.2°C

1.8 MPa, 退火, 3.18 mm 95.0°C

1.8 MPa, 退火, 12.7 mm 100°C

维卡软化温度

-- 107°C ASTM D1525 5

-- 96.0°C ISO 306/B50

线形热膨胀系数 - 流动 (-30 到 30°C) 9.0E-5cm/cm/°C ASTM D696

RTI Elec (1.57 mm) 60.0°C UL 746

RTI Imp (1.57 mm) 60.0°C UL 746

RTI (1.57 mm) 60.0°C UL 746

可燃性 额定值单位制 测试方法

燃烧速率 6 53mm/min SAE J1685

UL 阻燃等级 UL 94

1.57 mm HB

3.18 mm HB

注射 额定值单位制

干燥温度

A 82.2 到 87.8°C

B 71.1 到 76.7°C

干燥时间

A 2.0hr

B 4.0hr

建议的最大水分含量 < 0.10%

建议注射量 50 到 75%

建议的最大回制料比例 20%

料筒后部温度 235 到 249°C

料筒中部温度 241 到 254°C

料筒前部温度 246 到 260°C

射嘴温度 246 到 260°C

加工（熔体）温度 246 到 266°C

模具温度 43.3 到 65.6°C

注塑压力 68.9 到 110MPa

注射速度 快速

背压 0.345 到 0.689MPa

锁模力 2.8 到 5.5kN/cm²

垫层 < 6.35mm

螺杆长径比 20.0:1.0

螺杆压缩比 2.5:1.0

注射说明

Hold Pressure: 50 to 75% of Injection Pressure

Screw Speed: Moderate

 

 

 