Technical Data

 

产品说明

 

Jamplast high gloss resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. Jamplast ABS resins are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming processes.

 

Jamplast ABS resins are designed to offer a wide range of impact strengths and melt flow rates to meet the needs of the durables injection molding markets. This product offers typical Izod impact strength values from 4 to 7.5 ft-lb/in and melt flow rates ranging from 2.5 to 7.0 g/10 min. The gloss values are typically greater than 95% on the 60° Gardner scale for the highest gloss resins and greater than 90% for those products having a broader range of gloss.

 

Jamplast ABS resin offers a broader range of gloss while maintaining medium impact strength with a medium melt flow rate.

 

总体

 

材料状态 • 已商用：当前有效

供货地区 • 北美洲

形式 • 粒子

加工方法 • 挤出 • 注射成型

 

物理性能 额定值单位制 测试方法

比重 1.04g/cm³ ASTM D792

收缩率 - 流动 0.40 到 0.70% ASTM D955

机械性能 额定值单位制 测试方法

拉伸模量 2 2240MPa ASTM D638

抗张强度 2 ASTM D638

屈服 44.8MPa

断裂 31.0MPa

伸长率 2 (断裂) 40% ASTM D638

弯曲模量 3 2550MPa ASTM D790

弯曲强度 3 75.8MPa ASTM D790

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度 4 ASTM D256

-18°C, 3.18 mm 130J/m

23°C, 3.18 mm 320J/m

装有测量仪表的落镖冲击 5 ASTM D3763

-18°C, 3.18 mm, Peak Energy 26.0J

-18°C, 3.18 mm, Total Energy 31.6J

23°C, 3.18 mm, Peak Energy 33.9J

23°C, 3.18 mm, Total Energy 55.4J

热性能 额定值单位制 测试方法

载荷下热变形温度 ASTM D648

0.45 MPa, 未退火, 3.18 mm 92.2°C

1.8 MPa, 未退火, 3.18 mm 76.7°C

维卡软化温度 106°C ASTM D1525

线形热膨胀系数 - 流动 7.9E-5cm/cm/°C ASTM D696

可燃性 额定值单位制 测试方法

UL 阻燃等级 (1.47 mm) HB UL 94

光学性能 额定值单位制 测试方法

Gardner光泽度 (60°) 90 ASTM D523

 

Jamplast JPHGABS

丙烯腈丁二烯苯乙烯

Jamplast, Inc.

注射 额定值单位制

干燥温度 82.2 到 87.8°C

干燥时间 2.0 到 4.0hr

建议的最大水分含量 0.10%

加工（熔体）温度 218 到 274°C

模具温度 26.7 到 60.0°C

背压 0.345 到 3.45MPa

锁模力 2.8 到 6.9kN/cm²

螺杆长径比 20.0:1.0

螺杆压缩比 1.5:1.0 至 3.5:1.0

 

 

 

 