POLYLAC® PA-763
丙烯腈丁二烯苯乙烯
CHI MEI CORPORATION
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Technical Data
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
总体
|
|
|
|
|
|
|
|
材料状态
|
• 已商用:当前有效
|
|
|
|
|
|
|
|
• Technical Datasheet - ISO (English)
|
|
|
|
|
|
资料 1
|
• Technical Datasheet - ASTM (English)
|
|
|
|
|
|
|
• Processing (English)
|
|
|
|
|
|
|
UL 黄卡 2
|
• E56070-508235
|
|
|
|
|
|
|
搜索 UL 黄卡
|
• CHI MEI CORPORATION
|
|
|
|
|
|
|
• POLYLAC®
|
|
|
|
|
|
|
|
|
|
|
|
|
|
供货地区
|
• 北美洲
|
• 拉丁美洲
|
• 欧洲
|
|
|
|
• 非洲和中东
|
• 南美洲
|
• 亚太地区
|
|
|
|
|
|
|
|
RoHS 合规性
|
• RoHS 合规
|
|
|
|
|
|
|
加工方法
|
• 注射成型
|
|
|
|
|
|
|
|
|
|
|
|
|
|
物理性能
|
|
额定值单位制
|
测试方法
|
|
|
|
比重
|
|
|
|
|
|
--
|
|
1.19g/cm³
|
ASTM D792
|
|
|
|
23°C
|
|
1.19g/cm³
|
ISO 1183
|
|
|
|
熔流率
|
|
|
ASTM D1238
|
|
|
|
200°C/5.0 kg
|
|
2.8g/10 min
|
|
|
|
|
|
220°C/10.0 kg
|
|
30g/10 min
|
|
|
|
|
|
溶化体积流率(MVR) (220°C/10.0 kg)
|
|
30.0cm³/10min
|
ISO 1133
|
|
|
|
机械性能
|
|
额定值单位制
|
测试方法
|
|
|
|
拉伸应力
|
|
|
|
|
|
|
|
屈服
|
|
41.0MPa
|
ISO 527-2/50
|
|
|
|
断裂
|
|
32.0MPa
|
ISO 527-2/50
|
|
|
|
3.00 mm 4
|
|
38.7MPa
|
ASTM D638
|
|
|
|
伸长率
|
|
|
|
|
|
|
|
断裂, 3.00 mm 4
|
|
30%
|
ASTM D638
|
|
|
|
断裂
|
|
15%
|
ISO 527-2/50
|
|
|
|
弯曲模量
|
|
|
|
|
|
|
|
6.00 mm 5
|
|
2450MPa
|
ASTM D790
|
|
-- 6
|
|
2000MPa
|
ISO 178
|
|
|
|
弯曲强度
|
|
|
|
|
|
|
|
6.00 mm 5
|
|
60.8MPa
|
ASTM D790
|
|
-- 6
|
|
59.0MPa
|
ISO 178
|
|
|
|
冲击性能
|
|
额定值单位制
|
测试方法
|
|
|
|
简支梁缺口冲击强度
|
|
20kJ/m²
|
ISO 179
|
|
|
|
悬壁梁缺口冲击强度
|
|
|
|
|
|
|
|
23°C, 3.00 mm
|
|
240J/m
|
ASTM D256
|
|
|
|
23°C, 6.00 mm
|
|
200J/m
|
ASTM D256
|
|
--
|
|
20kJ/m²
|
ISO 180/1A
|
|
|
|
硬度
|
|
额定值单位制
|
测试方法
|
|
|
|
洛氏硬度 (R 计秤)
|
|
98
|
ASTM D785
|
|
|
|
球压硬度 (H 358/30)
|
|
80.0MPa
|
ISO 2039-1
|
|
|
|
热性能
|
|
额定值单位制
|
测试方法
|
|
热变形温度
1.8 MPa, 未退火
1.8 MPa, 未退火
1.8 MPa, 退火
85.0°C
86.0°C
96.0°C
ASTM D648 ISO 75-2/A
ASTM D648 ISO 75-2/A
POLYLAC® PA-763
丙烯腈丁二烯苯乙烯
CHI MEI CORPORATION
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
热性能
|
|
额定值单位制
|
测试方法
|
|
|
|
|
|
|
维卡软化温度
|
|
|
|
|
|
--
|
|
104°C
|
ASTM D1525 7
|
|
--
|
|
103°C
|
ISO 306/A50
|
|
--
|
|
96.0°C
|
ISO 306/B50
|
|
|
|
可燃性
|
|
额定值单位制
|
测试方法
|
|
|
|
UL 阻燃等级
|
|
|
UL 94
|
|
|
|
1.50 mm
|
|
V-0
|
|
|
|
|
|
1.60 mm
|
|
V-0
|
|
|
|
|
|
2.50 mm
|
•
|
5VB
|
|
|
|
|
|
•
|
5VA
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
注射
|
|
额定值单位制
|
|
|
|
|
|
干燥温度
|
|
80.0 到 85.0°C
|
|
|
|
|
|
干燥时间
|
|
2.0 到 4.0hr
|
|
|
|
|
|
螺筒后部温度
|
|
180 到 210°C
|
|
|
|
|
|
螺筒中部温度
|
|
190 到 220°C
|
|
|
|
|
|
螺筒前部温度
|
|
190 到 220°C
|
|
|
|
|
|
模具温度
|
|
40.0 到 70.0°C
|
|
|
|
|
|
注塑温度
|
|
4.90 到 7.85MPa
|
|
|
|
|
|
保压
|
|
1.96 到 4.90MPa
|
|
|
|
|
|
背压
|
|
0.490 到 0.981MPa
|
|
|
|
备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料;不过您可以从供应商处了解最新资料。
2 UL 黄卡含有 UL 验证的易燃性和电气特性。UL IDES 持续努力在 Prospector 中将黄卡链接至单个塑料材料,然而此列表可能未包括所有相应链接。重要的是,我们对 Prospector 中找到的这些黄卡和塑料材料之间的关联进行验证。如需完整的黄卡列表,请访问 UL 黄卡搜索。
3 一般属性:这些不能被视为规格。
4 6.0 mm/min
5 2.8 mm/min
6 2.0 mm/min
7 标准 A (50°C/h)
|