POLYLAN AT5500
|
|
|
|
|
|
|
|
|
|
|
|
|
丙烯腈丁二烯苯乙烯
|
|
|
|
|
|
|
|
|
|
|
|
|
POLYMA Kunststoff GmbH & Co. KG
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Technical Data
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
总体
|
|
|
|
|
|
|
|
|
材料状态
|
• 已商用:当前有效
|
|
|
|
|
|
|
|
资料 1
|
• Technical Datasheet (English)
|
|
|
|
|
|
|
|
供货地区
|
• 欧洲
|
|
|
|
|
|
|
|
UL 档案号
|
• E162823
|
|
|
|
|
|
|
|
外观
|
• 清晰/透明
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
物理性能
|
额定值 单位制
|
测试方法
|
|
|
|
|
|
密度
|
1.07g/cm³
|
ISO 1183
|
|
|
|
|
|
熔流率
|
|
ASTM D1238
|
|
|
|
|
|
200°C/10.0 kg
|
26g/10 min
|
ISO 1133
|
|
|
|
|
|
|
|
|
|
|
|
|
200°C/5.0 kg
|
2.1g/10 min
|
|
|
|
|
|
|
|
机械性能
|
额定值 单位制
|
测试方法
|
|
|
|
|
|
拉伸模量 (23°C)
|
2160MPa
|
ASTM D638
|
|
|
|
|
|
ISO 527-2
|
|
|
|
|
|
|
|
|
|
|
|
|
抗张强度 (屈服, 23°C)
|
44.0MPa
|
ASTM D638
|
|
|
|
|
|
ISO 527-2
|
|
|
|
|
|
|
|
|
|
|
|
|
弯曲强度 (23°C)
|
72.0MPa
|
ASTM D790
|
|
|
|
|
|
ISO 178
|
|
|
|
|
|
|
|
|
|
|
|
|
冲击性能
|
额定值 单位制
|
测试方法
|
|
|
|
|
|
悬壁梁缺口冲击强度 (23°C, 6.35 mm)
|
150J/m
|
ASTM D256
|
|
|
|
|
|
硬度
|
额定值 单位制
|
测试方法
|
|
|
|
|
|
洛氏硬度 (R 计秤, 23°C)
|
105
|
ASTM D785
|
|
|
|
|
|
ISO 2039-2
|
|
|
|
|
|
|
|
|
|
|
|
|
热性能
|
额定值 单位制
|
测试方法
|
|
|
|
|
|
热变形温度
|
|
|
|
|
|
|
|
|
1.8 MPa, 未退火, 12.7 mm
|
87.0°C
|
ASTM D648
|
|
|
|
|
|
1.8 MPa, 未退火
|
87.0°C
|
ISO 75-2/A
|
|
|
|
|
|
1.8 MPa, 退火, 12.7 mm
|
99.0°C
|
ASTM D648
|
|
|
|
|
|
1.8 MPa, 退火
|
99.0°C
|
ISO 75-2/A
|
|
|
|
|
|
维卡软化温度
|
102°C
|
ISO 306/A
|
3
|
|
|
|
|
ASTM D1525
|
|
|
|
|
可燃性
|
额定值 单位制
|
测试方法
|
|
|
|
|
|
UL 阻燃等级 (1.59 mm)
|
HB
|
UL 94
|
|
|
|
备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料;不过您可以从供应商处了解最新资料。
2 一般属性:这些不能被视为规格。
3 压 力1 (10N)
|